web analytics
Facade Brick Develop a hairline crack - Forno Bravo Forum: The Wood-Fired Oven Community


1 of 3 < >

Forum Page Loading Response

Forum Members:

We have received feedback regarding recent issues with page loading response time. We believe the slow response issue stems from the analytics we added with the new Forum. We are in the process of reconfiguring those elements and, after an approximate 24-hour time period for the reconfiguration to run, we anticipate a return to normal page load times. Thank you for your patience!
2 of 3 < >


Hello, Forno Bravo Community Forum members.

As many may have noticed already, the Community Forum site was briefly down today. While working on scheduled routine maintenance, we encountered an error when trying to add a software update. As the site is now back up and running, some of you may notice that some recent data has been misplaced from November 10th up to today. We are currently working on resolving the issue. The forum has full operational capabilities and we encourage all forum members to continue actively posting in the threads.

We apologize for any inconvenience that this issue may have caused you. The Forno Bravo family values each and every member of our community. If you have any issues or concerns, please feel free to let us know on our issues thread here:


Thank you for understanding.
3 of 3 < >

Forno Bravo Forum Thread Message

Hello, Forno Bravo Community Forum Members!

The Forno Bravo team has heard the feedback in regards to the community forum. We wanted to take the time to re-enforce our commitment to a fully engaged Forum with professional moderation.

Our top priority as a company is to fix all forum errors and issues that you are experiencing. As we are swiftly working on these problems, we want to say that we highly value the Forum Bravo Community Forum and every single community forum member.

We have set up this thread so that every member can address any concerns, issues and questions about the forum. Please feel free to ask whatever you would like in regards to the forum; let us know what issues you are experiencing so we can work on resolving them as fast as possible. However, we stress that we would like constructive engagement, so please be specific about the issue you are experiencing.

Thank you for all of your patience and continued support.

Link to topic: http://www.fornobravo.com/community/...with-new-forum
See more
See less

Facade Brick Develop a hairline crack

  • Filter
  • Time
  • Show
Clear All
new posts

  • Facade Brick Develop a hairline crack

    Question for those on the forum who have built a pompei style brick oven. I fired mine up for the 3rd time this past weekend. I built a somewhat larger fire this time but still not hot enough to cook in it. Oven got to about 450F.

    I notice the brick facade developed a hairline crack in the mortar. This crack travels horizontally across the facade on both sides of the oven door and is at the level of the brick lintel holding up the bricks for the chimney. I was surprised to see it as I have been building up the fires. My first oven had done the same thing but I had an arched entry way in the oven and a square one on the facade. The arched entry way had a thin piece of metal bent in the shape of the arch and was permanent in the oven. When this had happened that time I exchange emails with Alan Scott and he thought maybe the heat expanding the metal that was arched caused it to lift the facade and develop the crack. This time I have a square oven entry with brick lintel and an outer facade that is arched with no metal (self standing) and again I get this crack. It never amounted to any more than that the first time but it sure takes away from the all the hard work. Anyon else have similar experiences? Thx.
    Check out my build at:

  • #2
    in my (long) thread containing all of my building pictures, i posted about this same thing happening. the header over my doorway opening is archbrick, rather than a solid lintel, and there is no metal involved. when my oven fired up and moved around with expansion/contraction, a crack developed all the way around the dome, ending up at either corner of my arch, right where it turned sharply downward.

    i think the primary thing happening here, is that when initially fired, the bricks expand and move around a bit, and decide that they would prefer a different orientation than how we oh-so-carefully laid them. the refractory masons will tell you this is normal, and is one of the reasons for curing the oven. however, what worried me, is that my crack found a clear path all of the way around, therefore allowing that section of the arch header to creep forward a bit.

    in your design, if i'm understanding correctly, the expansion/lateral force of the top section of the dome could do the same thing with your lintel---the bricks heat up and expand and they all push against each other. the weakest point is going to give, and that point in this case appears to be where the lintel ties in with the rest of the dome, and the result is that the lintel/adjoining facade breaks loose from its surroundings.

    unless it seems to have expanded to the point where something may be structurally compromised, i wouldn't worry about it. apply fireplace cement...but keep an eye on it!
    overdo it or don't do it at all!


    • #3
      Bond breaks

      This also came up in the brick-oven group and I posted a note about it in answer to a query. (Alan seems to have disappeared from the group again leaving me as the only other brick designer -- Kiko's an earthenware guy.)

      Here's the relevant msg thread:

      --- In brick-oven@yahoogroups.com, "ovenenth" <ovenenth@y...> wrote:
      > The facade is common clay brick (not fire brick). How is the thermal
      > break introduced? It is too late for this one but interesting to know
      > how one does this?

      ### You use either an expansion joint or a bond break. The expansion
      joint uses an elastic medium like a neoprene or rubber pad in place of
      the mortar & then a flexible sealant to keep the water out. The bond
      break places a separation layer between the disimilar materials,
      usually something like building paper or flashing, to allow for a slip
      plane. In this case you'd keep an air gap between the firebrick & the
      common brick to act as the thermal bond break. Some folks will also
      use a different joint called a "control" joint that is designed to
      crack (it uses inflexible joint materials instead of rubber or
      neoprene). The idea being that you put this type in a place within the
      structure where it won't affect the structural integrity or aesthetics
      - kind of "it's going to crack anyway so I'm going to make it crack
      where I want it to crack and no one will see it."