Custom Mortar Mix - Forno Bravo Forum: The Wood-Fired Oven Community



New Forno Bravo Forum Feature

Forno Bravo Forum Community,

You will notice a new forum at the top of the main page called, "Ask Me Anything". This forum will be used for live one hour "Ask Me Anything" (AMA) sessions hosted by people who are knowledgeable in different areas pertaining to wood fired ovens. How it works:
- Each AMA will have a "sticky" thread where the community can post questions they would like answered during the live session. This will allow everyone to participate even if you can't be online for the live session. These questions will not be answered by the host until the live AMA; if you need an answer quickly, you should post it in the appropriate Forum area for the community to respond.
- Another thread will be posted for the live AMA. Registered users who are logged in during the live session can interact with the host by asking questions and receiving responses.
- The live thread will remain in the AMA forum to view after the session.

To kick off our AMA feature, we have invited author, chef and master bread maker and host of Pizza Quest, Peter Reinhart, to be our first host! Peter will be in the Forum on Monday, February 15th, from 7:00 - 8:00 pm EST. If you are unable to be online during the live session, you can post your questions in the sticky post. Peter will answer those questions during the live session on February 15th. You can view Peter's answers to your questions as well as what happened during the live session in the session thread.

We hope you enjoy this new feature! Please let us know if there is a topic that you'd like to have as an AMA and we'll look for a host!

Forno Bravo
See more
See less

Custom Mortar Mix

  • Filter
  • Time
  • Show
Clear All
new posts

  • Custom Mortar Mix

    Foundation is complete and ready to buiild the dome. I have searched this site and other sites looking for ratios for mortar. I am on a budget and don't want to spend $50 a bag There are several points of view. FB suggests 3-1-1-1. Other sites suggest a ratio of 10-6-2-3. which increase the ratio of fire clay and lime..Thoughts?

  • #2
    Re: Custom Mortar Mix

    I used the 3-1-1-1 and it worked fine. I kept it wet with damp towels while it cured and it set up nicely.

    You can alter it, I added a little extra lime, but I do not think it is needed. I began with the exact formula at first, because I had no background with refractory mortar, then I began to play a little. Would use it again if I build another oven.

    Many people on here have used the formula and seemed to have liked working with it. Plus it was way cheaper then buying premixed refrac mortar.

    I switched fireclay during my build from Alsey to Superior. I liked the Alsey way more. It was smoother and seemed to mix better with water. But the Superior was fine after I got used to it and adjusted my routine.

    Good luck.

    "Leave the gun. Take the cannoli." - Peter Clemenza


    • #3
      Re: Custom Mortar Mix

      If you are looking for what works, just about everyone on this forum that has used "homebrew" mortar went with 3-1-1-1 and had good luck. I would say it is probably not worth it to spend much time looking for an alternative
      My build progress
      My WFO Journal on Facebook
      My dome spreadsheet calculator


      • #4
        Re: Custom Mortar Mix

        Thanks. I will proceed with the 3-1-1-1.


        • #5
          Re: Custom Mortar Mix

          I started out with 3-1-1-1, and later started adding a bit more fireclay (an idea taken from CheeseSteak), making it closer to 3-1.5-1-1. Mortar consistency and stickiness was better with more clay.
          My build: http://www.fornobravo.com/forum/f8/3...-dc-18213.html


          • #6
            Re: Custom Mortar Mix

            I started out with 3-1-1-1, and later started adding a bit more lime after reading here of lime's contribution to maintaining mortar integrity after the portland has burned out. My slight additions of lime (and fireclay) were not measurable, more like 'a little more for Santa'.

            Here is a discussion of the (refractory) properties of the individual components that go into the classic 3-1-1-1.